Products Produced in Narlı Factory:
Portland Cement carries clinker, gypsum as setting regulator and it’s been grinded together with minor additional component. Complies with TS EN 197-1: 2012 standard.
It has early strength and ultimate strength due to it is high clinker content.
Portland Cement carries clinker, gypsum as setting regulator and it is grinded together with minor additional component. Complies with TS EN 197-1: 2012 standard, is a cement with a 28 days compressive strength of at least 52.5 MPa.
It has early strength and ultimate strength.
Portland Cement clinker carries gypsum as a regulator, 12-20% contribution (Puzolan - Limestone) and it’s been grinded together with minor additional component. Complies with TS EN 197-1: 2012 standard.
Due to its fine workability, it is highly machinable and tightens the micropores in the concrete. Improves impermeability and balances the heat of hydration. It is preferred especially in hot weather and mass concrete.
Portland Cement clinker carries gypsum as a regulator, % 6-20 (Puzolan) contribution and it’s been grinded together with minor additional component. Complies with TS EN 197-1: 2012 standard.
Thanks to it’s high machinability has the property of early strength and ultimate strength. It is preferred in concrete casting and mass concrete in open air.
Portland Cement clinker carries gypsum as a regulator, % 21-35 (Puzolan - Limestone) contribution and it’s been grinded together with minor additional component. Complies with TS EN 197-1: 2012 standard.
It has high workability and durability and is preferred for applications such as plaster, screed and mortar.
Products Produced in Adıyaman Factory:
Portland Cement carries clinker, gypsum as setting regulator and it’s been grinded together with minor additional component. Complies with TS EN 197-1: 2012 standard.
It has early strength and ultimate strength due to it is high clinker content.
Portland Cement with a maximum C3A content of 5% carries; clinker, gypsum as setting regulator and it’s been grinded together with minor additional component. Complies with TS EN 197-1: 2012 standard.
Due to it’s low C3A effect It has the property of sulphate resistant. It is highly preferred in applications such as sea water, sewage, etc. that are exposed to high sulphate.
Portland cement clinker is a cementitious admixture conforming to TS EN 197 -1: 2012 standard which is obtained by grinding with gypsum, 21-35% additive (Puzolan - Limestone) and minor additive as a setting regulator.
It has high workability and durability and is preferred in applications such as plaster, screed and mortar.
Oil Well Cement (OWC), also known as Oil Well Cement, which provides rapid and desired strength under high temperature, shows high sulphate resistance and has a suitable thickening time, is widely used in oil drilling wells, geothermal power plants and soda wells.
Products Produced in Bartın Factory:
Portland Cement carries clinker, gypsum as setting regulator and it’s been grinded together with minor additional component. Complies with TS EN 197-1: 2012 standard.
It has early strength and ultimate strength due to it is high clinker content.
Portland Cement clinker, gypsum and up to 5% minor additive material are grinded together and produced in accordance with TS EN 197 -1 / March: 2002 “Cement - Part 1: General Cements - Composition, Properties and Conformity Criteria” standard. Cement with a compressive strength of at least 30 days and a minimum compressive strength of 28 days and a minimum of 52.5 MPa.
It has the feature of early strength and ultimate strength.
Portland Cement clinker, gypsum, 36-55% additive (Tras - Fly Ash) and up to 5% minor additional ingredient co-grinding TS EN 197 -1 / March: 2002 “Cement - Department It is a cement produced according to 1: General Cements Composition, Properties and Conformity Criteria ”, with a 2-day compressive strength of at least 10 and a 28-day compressive strength of at least 32.5 MPa and a maximum of 52.5 MPa. As it contains high additives, its hydration temperature is low, it is more resistant to alkali-aggregate reaction and chemical external effects.
Portland Cement with a maximum C3A content of 5% carries; clinker, gypsum as setting regulator and it’s been grinded together with minor additional component. Complies with TS EN 197-1: 2012 standard.
Due to it’s low C3A effect It has the property of sulphate resistant. It is highly preferred in applications such as sea water, sewage, etc. that are exposed to high sulphate.
Products Produced in Ereğli Grinding Plant:
Portland Fly Ash Cement is the result of grinding together Portland Cement clinker, gypsum, 6-20% additive (Fly Ash) and up to 5% minor additional component material. TS EN 197 -1 / March: 2002 “Cement - Section 1: General Cements - Composition, Properties and Conformity Criteria" standard, manufactured in accordance with the 2-day compressive strength of at least 20 and 28-day compressive strength of at least 42.5 MPa and maximum 62.5 MPa.
Sulphate Resistant Pozzolanic Cement is a result of grinding together Portland Cement clinker, gypsum, 36-55% additive (Fly Ash) and up to 5% minor additional component material. TS EN 197 -1 / March: 2002 “Cement - Section 1: General Cements Composition, Properties and Conformity Criteria" standard, manufactured in accordance with the 2-day compressive strength of at least 10 and 28-day compressive strength of at least 32.5 MPa and maximum 52.5 MPa.
Since it contains high additives, it has a lower heat of hydration and is more resistant to alkali-aggregate reaction and external chemical effects.
Since it gains sulphate resistance thanks to its content, it can be used in environments exposed to high sulphate such as sea water and sewage.